glass-ceramics are fine-grained polycrystalline materials
obtained from a parent glass by controlled crystallization.
The glass-ceramics of the CaO-MgO-SiO2 system have been
extensively investigated for industrial applications because
they are common and inexpensive materials. Also, these
materials present good chemical resistance, high mechanical
properties, and a wide range of crystalline phases that result
from the surface devitrification of single-step temperature
treatment. Among the crystalline phases, diopside (CaMgSi2O6)
and enstatite (MgSiO3) phases are usually generated.
For multilayer packages applicable to lighting-emitting diodes
(LED) with high-power, the diopside-enstatite system could
be used due to its relatively low heat-treatment temperature
and high thermal conductivity, which could make this material
applicable in the process of co-firing with low-melting point
electrodes (Ag = 960oC, Cu = 1050oC) and to obtain fast heat
dissipations in LED chips.
In our preliminary experiment, the diopside-enstatite system
of 0.9CaMgSi2O6-0.1MgSiO3 glass-ceramics heat-treated at
800oC for 5 h had thermal properties that were better than
those of the other compositions of the CaMgSi2O6-MgSiO3
system. Since the thermal properties of the glass-ceramics
were found to change with heat-treatment temperature due
to changes of crystallization, the dependence of the thermal
properties on the degree of crystallization of 0.9CaMgSi2O6-
0.1MgSiO3 glass-ceramics should be investigated as a function شیشه ,سرامیک، مواد ریز دانه چندبلوری
از شیشه ای پدر و مادر توسط تبلور کنترل شده به دست آمده است.
شیشه سرامیک از سیستم کائو-MgO در-SiO2 بوده است
گسترده ای برای کاربردهای صنعتی به دلیل بررسی
مواد مشترک و ارزان هستند. همچنین، این
مواد در حال حاضر مقاومت در برابر مواد شیمیایی، مکانیکی بالا
خواص، و طیف گسترده ای از فازهای بلوری که در نتیجه
به از devitrification سطح دمای تک مرحله ای
درمان است. در بین فازهای بلورین، diopside (CaMgSi2O6)
و) فاز enstatite (MgSiO3 در معمولا تولید می شود.
برای بسته های چند قابل انطباق با روشنایی و دیودهای ساطع
(LED) با قدرت بالا، سیستم diopside-enstatite
مورد استفاده قرار گیرد با توجه به نسبتا کم عملیات حرارتی، دمای آن
و هدایت حرارتی بالا، که می تواند این مواد را
در روند همکاری شلیک با نقطه ذوب پایین
الکترود (نقره = 960oC، مس = 1050oC) و برای به دست آوردن گرما سریع
dissipations در تراشه های LED.
در آزمایش اولیه، سیستم diopside-enstatite
0.9CaMgSi2O6-0.1MgSiO3 شیشه سرامیک حرارت قرار می گیرند در
800oC برای 5 خواص ساعت و حرارتی بود که بهتر از
کسانی که از ترکیب دیگر CaMgSi2O6-MgSiO3 می
سیستم. از آنجا که خواص حرارتی شیشه و سرامیک
با عملیات حرارتی دمای پایین به دلیل تغییر یافت شد
تغییر تبلور، وابستگی حرارتی
خواص در درجه تبلور 0.9CaMgSi2O6،
0.1MgSiO3 شیشه، سرامیک باید به عنوان یک تابع مورد بررسی قرار
obtained from a parent glass by controlled crystallization.
The glass-ceramics of the CaO-MgO-SiO2 system have been
extensively investigated for industrial applications because
they are common and inexpensive materials. Also, these
materials present good chemical resistance, high mechanical
properties, and a wide range of crystalline phases that result
from the surface devitrification of single-step temperature
treatment. Among the crystalline phases, diopside (CaMgSi2O6)
and enstatite (MgSiO3) phases are usually generated.
For multilayer packages applicable to lighting-emitting diodes
(LED) with high-power, the diopside-enstatite system could
be used due to its relatively low heat-treatment temperature
and high thermal conductivity, which could make this material
applicable in the process of co-firing with low-melting point
electrodes (Ag = 960oC, Cu = 1050oC) and to obtain fast heat
dissipations in LED chips.
In our preliminary experiment, the diopside-enstatite system
of 0.9CaMgSi2O6-0.1MgSiO3 glass-ceramics heat-treated at
800oC for 5 h had thermal properties that were better than
those of the other compositions of the CaMgSi2O6-MgSiO3
system. Since the thermal properties of the glass-ceramics
were found to change with heat-treatment temperature due
to changes of crystallization, the dependence of the thermal
properties on the degree of crystallization of 0.9CaMgSi2O6-
0.1MgSiO3 glass-ceramics should be investigated as a function شیشه ,سرامیک، مواد ریز دانه چندبلوری
از شیشه ای پدر و مادر توسط تبلور کنترل شده به دست آمده است.
شیشه سرامیک از سیستم کائو-MgO در-SiO2 بوده است
گسترده ای برای کاربردهای صنعتی به دلیل بررسی
مواد مشترک و ارزان هستند. همچنین، این
مواد در حال حاضر مقاومت در برابر مواد شیمیایی، مکانیکی بالا
خواص، و طیف گسترده ای از فازهای بلوری که در نتیجه
به از devitrification سطح دمای تک مرحله ای
درمان است. در بین فازهای بلورین، diopside (CaMgSi2O6)
و) فاز enstatite (MgSiO3 در معمولا تولید می شود.
برای بسته های چند قابل انطباق با روشنایی و دیودهای ساطع
(LED) با قدرت بالا، سیستم diopside-enstatite
مورد استفاده قرار گیرد با توجه به نسبتا کم عملیات حرارتی، دمای آن
و هدایت حرارتی بالا، که می تواند این مواد را
در روند همکاری شلیک با نقطه ذوب پایین
الکترود (نقره = 960oC، مس = 1050oC) و برای به دست آوردن گرما سریع
dissipations در تراشه های LED.
در آزمایش اولیه، سیستم diopside-enstatite
0.9CaMgSi2O6-0.1MgSiO3 شیشه سرامیک حرارت قرار می گیرند در
800oC برای 5 خواص ساعت و حرارتی بود که بهتر از
کسانی که از ترکیب دیگر CaMgSi2O6-MgSiO3 می
سیستم. از آنجا که خواص حرارتی شیشه و سرامیک
با عملیات حرارتی دمای پایین به دلیل تغییر یافت شد
تغییر تبلور، وابستگی حرارتی
خواص در درجه تبلور 0.9CaMgSi2O6،
0.1MgSiO3 شیشه، سرامیک باید به عنوان یک تابع مورد بررسی قرار
+ نوشته شده در دوشنبه پانزدهم خرداد ۱۳۹۱ ساعت 12:17 توسط حسن بابالویی
|